Carbon And Alloy Steel Cut-To-Length Plate from South Korea (C-580-888)

Scope Description:

The products covered by this investigation are certain carbon
and alloy steel hot-rolled or forged flat plate products not in
coils, whether or not painted, varnished, or coated with plastics or
other non-metallic substances (cut-to-length plate). Subject
merchandise includes plate that is produced by being cut-to-length
from coils or from other discrete length plate and plate that is
rolled or forged into a discrete length. The products covered
include (1) Universal mill plates (i.e., flat-rolled products rolled
on four faces or in a closed box pass, of a width exceeding 150 mm
but not exceeding 1250 mm, and of a thickness of not less than 4 mm,
which are not in coils and without patterns in relief), and (2) hot-
rolled or forged flat steel products of a thickness of 4.75 mm or
more and of a width which exceeds 150 mm and measures at least twice
the thickness, and which are not in coils, whether or not with
patterns in relief. The covered products described above may be
rectangular, square, circular or other shapes and include products
of either rectangular or non-rectangular cross-section where such
non-rectangular cross-section is achieved subsequent to the rolling
process, i.e., products which have been ``worked after rolling''
(e.g., products which have been beveled or rounded at the edges).
For purposes of the width and thickness requirements referenced
above, the following rules apply:
(1) Except where otherwise stated where the nominal and actual
thickness or width measurements vary, a product from a given subject
country is within the scope if application of either the nominal or
actual measurement would place it within the scope based on the
definitions set forth above unless the product is already covered by
an order existing on that specific country (i.e., Certain Hot-Rolled
Steel Flat Products from Brazil and the Republic of Korea: Amended
Final Affirmative Countervailing Duty Orders, 81 FR 67960 (October
3, 2016)); and
(2) where the width and thickness vary for a specific product
(e.g., the thickness of certain products with non-rectangular cross-
section, the width of certain products with non-rectangular shape,
etc.), the measurement at its greatest width or thickness applies.
Steel products included in the scope of this investigation are
products in which: (1) Iron predominates, by weight, over each of
the other contained elements; and (2) the carbon content is 2
percent or less by weight.
Subject merchandise includes cut-to-length plate that has been
further processed in the subject country or a third country,
including but not limited to pickling, oiling, levelling, annealing,
tempering, temper rolling, skin passing, painting, varnishing,
trimming, cutting, punching, beveling, and/or slitting, or any other
processing that would not otherwise remove the merchandise from the
scope of the investigation if performed in the country of
manufacture of the cut-to-length plate.
All products that meet the written physical description, are
within the scope of this investigation unless specifically excluded
or covered by the scope of an existing order. The following products
are outside of, and/or specifically excluded from, the scope of this
investigation:
(1) Products clad, plated, or coated with metal, whether or not
painted, varnished or

[[Page 24105]]

coated with plastic or other non-metallic substances;
(2) military grade armor plate certified to one of the following
specifications or to a specification that references and
incorporates one of the following specifications:

MIL-A-12560,
MIL-DTL-12560H,
MIL-DTL-12560J,
MIL-DTL-12560K,
MIL-DTL-32332,
MIL-A-46100D,
MIL-DTL-46100-E,
MIL-46177C,
MIL-S-16216K Grade HY80,
MIL-S-16216K Grade HY100,
MIL-S-24645A HSLA-80;
MIL-S-24645A HSLA-100,
T9074-BD-GIB-010/0300 Grade HY80,
T9074-BD-GIB-010/0300 Grade HY100,
T9074-BD-GIB-010/0300 Grade HSLA80,
T9074-BD-GIB-010/0300 Grade HSLA100, and
T9074-BD-GIB-010/0300 Mod. Grade HSLA115,

except that any cut-to-length plate certified to one of the above
specifications, or to a military grade armor specification that
references and incorporates one of the above specifications, will
not be excluded from the scope if it is also dual- or multiple-
certified to any other non-armor specification that otherwise would
fall within the scope of this investigation;
(3) stainless steel plate, containing 10.5 percent or more of
chromium by weight and not more than 1.2 percent of carbon by
weight;
(4) CTL plate meeting the requirements of ASTM A-829, Grade E
4340 that are over 305 mm in actual thickness;
(5) Alloy forged and rolled CTL plate greater than or equal to
152.4 mm in actual thickness meeting each of the following
requirements:
(a) Electric furnace melted, ladle refined & vacuum degassed and
having a chemical composition (expressed in weight percentages):

Carbon 0.23-0.28,
Silicon 0.05-0.20,
Manganese 1.20-1.60,
Nickel not greater than 1.0,
Sulfur not greater than 0.007,
Phosphorus not greater than 0.020,
Chromium 1.0-2.5,
Molybdenum 0.35-0.80,
Boron 0.002-0.004,
Oxygen not greater than 20 ppm,
Hydrogen not greater than 2 ppm, and
Nitrogen not greater than 60 ppm;

(b) With a Brinell hardness measured in all parts of the product
including mid thickness falling within one of the following ranges:

(i) 270-300 HBW,
(ii) 290-320 HBW, or
(iii) 320-350HBW;

(c) Having cleanliness in accordance with ASTM E45 method A
(Thin and Heavy): A not exceeding 1.5, B not exceeding 1.0, C not
exceeding 0.5, D not exceeding 1.5; and
(d) Conforming to ASTM A578-S9 ultrasonic testing requirements
with acceptance criteria 2 mm flat bottom hole;
(6) Alloy forged and rolled steel CTL plate over 407 mm in
actual thickness and meeting the following requirements:
(a) Made from Electric Arc Furnace melted, Ladle refined &
vacuum degassed, alloy steel with the following chemical composition
(expressed in weight percentages):

Carbon 0.23-0.28,
Silicon 0.05-0.15,
Manganese 1.20-1.50,
Nickel not greater than 0.4,
Sulfur not greater than 0.010,
Phosphorus not greater than 0.020,
Chromium 1.20-1.50,
Molybdenum 0.35-0.55,
Boron 0.002-0.004,
Oxygen not greater than 20 ppm,
Hydrogen not greater than 2 ppm, and
Nitrogen not greater than 60 ppm;

(b) Having cleanliness in accordance with ASTM E45 method A
(Thin and Heavy): A not exceeding 1.5, B not exceeding 1.5, C not
exceeding 1.0, D not exceeding 1.5;
(c) Having the following mechanical properties:
(i) With a Brinell hardness not more than 237 HBW measured in
all parts of the product including mid thickness; and having a Yield
Strength of 75ksi min and UTS 95ksi or more, Elongation of 18% or
more and Reduction of area 35% or more; having charpy V at -75
degrees F in the longitudinal direction equal or greater than 15 ft.
lbs (single value) and equal or greater than 20 ft. lbs (average of
3 specimens) and conforming to the requirements of NACE MR01-75; or
(ii) With a Brinell hardness not less than 240 HBW measured in
all parts of the product including mid thickness; and having a Yield
Strength of 90 ksi min and UTS 110 ksi or more, Elongation of 15% or
more and Reduction of area 30% or more; having charpy V at -40
degrees F in the longitudinal direction equal or greater than 21 ft.
lbs (single value) and equal or greater than 31 ft. lbs (average of
3 specimens);
(d) Conforming to ASTM A578-S9 ultrasonic testing requirements
with acceptance criteria 3.2 mm flat bottom hole; and
(e) Conforming to magnetic particle inspection in accordance
with AMS 2301;
(7) Alloy forged and rolled steel CTL plate over 407 mm in
actual thickness and meeting the following requirements:
(a) Made from Electric Arc Furnace melted, ladle refined &
vacuum degassed, alloy steel with the following chemical composition
(expressed in weight percentages):

Carbon 0.25-0.30,
Silicon not greater than 0.25,
Manganese not greater than 0.50,
Nickel 3.0-3.5,
Sulfur not greater than 0.010,
Phosphorus not greater than 0.020,
Chromium 1.0-1.5,
Molybdenum 0.6-0.9,
Vanadium 0.08 to 0.12
Boron 0.002-0.004,
Oxygen not greater than 20 ppm,
Hydrogen not greater than 2 ppm, and
Nitrogen not greater than 60 ppm.

(b) Having cleanliness in accordance with ASTM E45 method A
(Thin and Heavy): A not exceeding 1.0(t) and 0.5(h), B not exceeding
1.5(t) and 1.0(h), C not exceeding 1.0(t) and 0.5(h), and D not
exceeding 1.5(t) and 1.0(h);
(c) Having the following mechanical properties: A Brinell
hardness not less than 350 HBW measured in all parts of the product
including mid thickness; and having a Yield Strength of 145ksi or
more and UTS 160ksi or more, Elongation of 15% or more and Reduction
of area 35% or more; having charpy V at -40 degrees F in the
transverse direction equal or greater than 20 ft. lbs (single value)
and equal or greater than 25 ft. lbs (average of 3 specimens);
(d) Conforming to ASTM A578-S9 ultrasonic testing requirements
with acceptance criteria 3.2 mm flat bottom hole; and
(e) Conforming to magnetic particle inspection in accordance
with AMS 2301.
At the time of the filing of the petition, there was an existing
countervailing duty order on certain cut-to-length carbon-quality
steel plate from Korea. See Final Affirmative Countervailing Duty
Determination: Certain Cut-to-Length Carbon-Quality Steel Plate From
the Republic of Korea, 64 FR 73,176 (Dep't Commerce Dec. 29, 1999),
as amended, 65 FR 6,587 (Dep't Commerce Feb. 10, 2000) (1999 Korea
CVD Order). The scope of the countervailing duty investigation with
regard to cut-to-length plate from Korea covers only (1) subject
cut-to-length plate not within the physical description of cut-to-
length carbon quality steel plate in the 1999 Korea CVD Order
regardless of producer or exporter, and (2) cut-to-length plate
produced and/or exported by those companies that were excluded or
revoked from the 1999 Korea CVD Order as of April 8, 2016. The only
revoked or excluded company is Pohang Iron and Steel Company, also
known as POSCO.
The products subject to the investigation are currently
classified in the Harmonized Tariff Schedule of the United States
(HTSUS) under item numbers: 7208.40.3030, 7208.40.3060,
7208.51.0030, 7208.51.0045, 7208.51.0060, 7208.52.0000,
7211.13.0000, 7211.14.0030, 7211.14.0045, 7225.40.1110,
7225.40.1180, 7225.40.3005, 7225.40.3050, 7226.20.0000, and
7226.91.5000.
The products subject to the investigation may also enter under
the following HTSUS item numbers: 7208.40.6060, 7208.53.0000,
7208.90.0000, 7210.70.3000, 7210.90.9000, 7211.19.1500,
7211.19.2000, 7211.19.4500, 7211.19.6000, 7211.19.7590,
7211.90.0000, 7212.40.1000, 7212.40.5000, 7212.50.0000,
7214.10.0000, 7214.30.0010, 7214.30.0080, 7214.91.0015, 7214.91.0016, 7214.91.0020
7214.91.0060, 7214.91.0090, 7225.11.0000, 7225.19.0000,
7225.40.5110, 7225.40.5130, 7225.40.5160, 7225.40.7000,
7225.99.0010, 7225.99.0090, 7226.11.1000, 7226.11.9060,
7226.19.1000, 7226.19.9000, 7226.91.0500, 7226.91.1530,
7226.91.1560, 7226.91.2530, 7226.91.2560, 7226.91.7000,
7226.91.8000, and 7226.99.0180.
The HTSUS subheadings above are provided for convenience and
customs purposes only. The written description of the scope of the
investigation is dispositive.