For purposes of this investigation, the products covered are certain hot-rolled flat-rolled carbon-quality steel products of a rectangular shape, of a width of 0.5 inch or greater, neither clad, plated, nor coated with metal and whether or not painted, varnished, or
coated with plastics or other non-metallic substances, in coils (whether or not in successively superimposed layers) regardless of thickness, and in straight lengths, of a thickness less than 4.75 mm and of a width measuring at least 10 times the thickness. Universal mill plate (i.e., flat-rolled products rolled on four faces or in a closed box pass, of a width exceeding 150 mm but not exceeding 1250 mm and of a thickness of not less than 4 mm, not in coils and without patterns in relief) of a thickness not less than 4.0 mm is not included within the scope of these investigations.
Specifically included in this scope are vacuum degassed, fully stabilized (commonly referred to as interstitial-free (``IF'')) steels, high strength low alloy (``HSLA'') steels, and the substrate for motor lamination steels. IF steels are recognized as low carbon steels with micro-alloying levels of elements such as titanium and/or niobium added to stabilize carbon and nitrogen elements. HSLA steels are recognized as steels with micro-alloying levels of elements such as chromium, copper, niobium, titanium, vanadium, and molybdenum. The substrate for motor lamination steels contains micro-alloying levels of elements such as silicon and aluminum.
Steel products to be included in the scope of this investigation, regardless of HTSUS definitions, are products in which: (1) iron predominates, by weight, over each of the other contained elements; (2) the carbon content is 2 percent or less, by weight; and (3) none of the elements listed below exceeds the quantity, by weight, respectively indicated:
1.80 percent of manganese, or
1.50 percent of silicon, or
1.00 percent of copper, or
0.50 percent of aluminum, or
1.25 percent of chromium, or
0.30 percent of cobalt, or
0.40 percent of lead, or
1.25 percent of nickel, or
0.30 percent of tungsten, or
0.012 percent of boron, or
0.10 percent of molybdenum, or
0.10 percent of niobium, or
0.41 percent of titanium, or
0.15 percent of vanadium, or
0.15 percent of zirconium.
All products that meet the physical and chemical description provided above are within the scope of this investigation unless otherwise excluded. The following products, by way of example, are outside and/or specifically excluded from the scope of this investigation:
<bullet> Alloy hot-rolled steel products in which at least one of the chemical elements exceeds those listed above (including e.g., ASTM specifications A543, A387, A514, A517, and A506).
<bullet> SAE/AISI grades of series 2300 and higher.
<bullet> Ball bearing steels, as defined in the HTSUS.
<bullet> Tool steels, as defined in the HTSUS.
<bullet> Silico-manganese (as defined in the HTSUS) or silicon electrical steel with a silicon level exceeding 1.50 percent.
<bullet> ASTM specifications A710 and A736.
<bullet> USS Abrasion-resistant steels (USS AR 400, USS AR 500).
<bullet> Hot-rolled steel coil which meets the following chemical, physical and mechanical specifications:
------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------
C Mn P S Si Cr Cu Ni
------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------
0.10-0.14%....................... 0.90% Max............ 0.025% Max........... 0.005% Max........... 0.30-0.50%........... 0.50-0.70%........... 0.20-0.40%.......... 0.20% Max.
------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------
Width = 44.80 inches maximum; Thickness = 0.063-0.198 inches;
Yield Strength = 50,000 ksi minimum; Tensile Strength =
70,000-88,000 psi.
<bullet> Hot-rolled steel coil which meets the following chemical,
physical and mechanical specifications:
------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------
C Mn P S Si Cr Cu Ni Mo
------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------
0.10-0.16%..................... 0.70-0.90%......... 0.025% Max........ 0.006% Max........ 0.30-0.50%........ 0.50-0.70%........ 0.25% Max......... 0.20% Max......... 0.21% Max
------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------
Width = 44.80 inches maximum; Thickness = 0.350 inches maximum;
Yield Strength = 80,000 ksi minimum; Tensile Strength = 105,000 psi
Aim.
<bullet> Hot-rolled steel coil which meets the following chemical,
physical and mechanical specifications:
------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------
C Mn P S Si Cr Cu Ni V(wt.) Cb
------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------
010.10-0.14%................... 11.30-1.80%..... 10.025% Max..... 1.005% Max...... 10.30-0.50%..... 10.50-0.70%..... 10.20-0.40%..... 10.20% Max...... 010.10 Max...... 0.08% Max
------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------
Width = 44.80 inches maximum; Thickness = 0.350 inches maximum;
Yield Strength = 80,000 ksi minimum; Tensile Strength = 105,000 psi
Aim.
<bullet> Hot-rolled steel coil which meets the following chemical,
physical and mechanical specifications:
[[Page 24331]]
------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------
C Mn P S Si Cr Cu Ni Nb Ca Al
------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------
0.15% Max..................... 1.40% Max...... 0.025% Max..... 0.010% Max.... 0.50% Max..... 1.00% Max..... 0.50% Max..... 0.20% Max..... 0.005% Min.... Treated....... 0.01-0.07%
------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------
Width = 39.37 inches; Thickness = 0.181 inches maximum; Yield
Strength = 70,000 psi minimum for thicknesses <ls-thn-eq> 0.148 inches
and 65,000 psi minimum for thicknesses >0.148 inches; Tensile Strength
= 80,000 psi minimum.
<bullet> Hot-rolled dual phase steel, phase-hardened, primarily with a ferritic-martensitic microstructure, contains 0.9 percent up to and including 1.5 percent silicon by weight, further characterized by either (i) tensile strength between 540 N/mm <SUP>2</SUP> and 640 N/mm <SUP>2</SUP> and an elongation percentage <gr-thn-eq>26 percent for thicknesses of 2 mm and above, or (ii) a tensile strength between 590 N/mm <SUP>2</SUP> and 690 N/mm <SUP>2</SUP> and an elongation
percentage <gr-thn-eq>25 percent for thicknesses of 2mm and above.
<bullet> Hot-rolled bearing quality steel, SAE grade 1050, in coils, with an inclusion rating of 1.0 maximum per ASTM E 45, Method A, with excellent surface quality and chemistry restrictions as follows:
0.012 percent maximum phosphorus, 0.015 percent maximum sulfur, and
0.20 percent maximum residuals including 0.15 percent maximum chromium.
<bullet> Grade ASTM A570-50 hot-rolled steel sheet in coils or cut
lengths, width of 74 inches (nominal, within ASTM tolerances),
thickness of 11 gauge (0.119 inch nominal), mill edge and skin passed,
with a minimum copper content of 0.20%.
The merchandise subject to these investigations is classified in the Harmonized Tariff Schedule of the United States (``HTSUS'') at subheadings: 7208.10.15.00, 7208.10.30.00, 7208.10.60.00, 7208.25.30.00, 7208.25.60.00, 7208.26.00.30, 7208.26.00.60,
7208.27.00.30, 7208.27.00.60, 7208.36.00.30, 7208.36.00.60, 7208.37.00.30, 7208.37.00.60, 7208.38.00.15, 7208.38.00.30, 7208.38.00.90, 7208.39.00.15, 7208.39.00.30, 7208.39.00.90, 7208.40.60.30, 7208.40.60.60, 7208.53.00.00, 7208.54.00.00, 7208.90.00.00, 7210.70.30.00, 7210.90.90.00, 7211.14.00.30,
7211.14.00.90, 7211.19.15.00, 7211.19.20.00, 7211.19.30.00, 7211.19.45.00, 7211.19.60.00, 7211.19.75.30, 7211.19.75.60, 7211.19.75.90, 7212.40.10.00, 7212.40.50.00, 7212.50.00.00. Certain hot-rolled flat-rolled carbon-quality steel covered by this investigation, including: vacuum degassed, fully stabilized; high strength low alloy; and the substrate for motor lamination steel may also enter under the following tariff numbers: 7225.11.00.00, 7225.19.00.00, 7225.30.30.50, 7225.30.70.00, 7225.40.70.00,
7225.99.00.90, 7226.11.10.00, 7226.11.90.30, 7226.11.90.60, 7226.19.10.00, 7226.19.90.00, 7226.91.50.00, 7226.91.70.00, 7226.91.80.00, and 7226.99.01.80. Although the HTSUS subheadings are provided for convenience and Customs purposes, the written description of the merchandise under investigation is dispositive.
Period of Investigation
The period of investigation (``POI'') is July 1, 1997 through June 30, 1998.
Edited April 11, 2012
HTS #7226.99.0000 has been replaced with 7226.99.0180. Scope modified to reflect this change in HTSUS |